Microtensile bond strengths of glass ionomer (polyalkenoate) cements to dentine using four conditioners

Abstract

Objectives: The purpose of this study was to measure the microtensile bond strengths of three glass ionomer cements to dentine (Photac-Fil Quick; Fuji II LC; Fuji IX GP) using four different conditioners (Ketac Conditioner; Dentin Conditioner; Cavity Conditioner; and an experimental conditioner, K-930). Methods: Superficial occlusal dentine of extracted human third molars was exposed, finished with wet 600-grit silicon carbide paper, and each of the above glass ionomer cements bonded using the four conditioners according to the manufacturers' instructions. After 24 h in tap water at 37°C, the teeth were sectioned to obtain 3-4 bar-shaped specimens. Ten specimens were prepared for each group and shaped to an hour-glass form of (1.2 ± 0.02) mm diameter. The specimens were mounted in ajig and stressed in tension at a crosshead speed of 1 mm/min until failure. The mean bond strengths were calculated and compared using one-way ANOVA and LSD tests, and the fracture modes were examined by scanning electron microscopy. Results: Mean microtensile bond strengths for Photac-Fil Quick were not significantly different from Fuji II LC for each of the conditioners used. However, the bond strengths for Photac-Fil Quick were significantly greater than Fuji II LC when no conditioner was applied. Mean microtensile bond strengths of conditioned specimens of Fuji II LC were significantly greater than non-conditioned specimens. Mean microtensile bond strengths of non-conditioned specimens of Fuji IX GP were not significantly different from conditioned specimens. The fracture mode of all specimens demonstrated mostly cohesive failure within the cement. Significance: The use of surface conditioners resulted in improvement in bond strength of Fuji II LC, while Photac-Fil Quick and Fuji IX GP showed no difference. © 2000 Elsevier Science Ltd. All rights reserved.