Ion release of the glass ionomer restoration with silver diamine fluoride dentin pretreatment

Abstract

Objective: To assess the fluoride and silver ion release of glass ionomer cement (GIC) restorations, including conventional GIC (CGIC) and resin-modified GIC (RMGIC) restorations, with 38 % silver diamine fluoride (SDF) solution dentin pretreatment. Methods: Eighty dentin blocks were allocated into 4 groups and restored with SDF+CGIC, CGIC, SDF+RMGIC and RMGIC, respectively. Each block was stored in deionized water at 37 °C for 2 years. Fluoride and silver ion concentration in storage solution was measured using ion-selective electrode and inductively coupled plasma-optical emission spectrometry for up to 2 years. The cross-sectional surfaces of restored dentin blocks were assessed by X-Ray diffraction analysis (XRD), scanning electron microscope (SEM) with energy-dispersive X-ray spectroscopy (EDS) after 1 week and 2 years, respectively. Results: The mean ± standard deviation (SD) of accumulative fluoride releasing in SDF+CGIC, CGIC, SDF+RMGIC and RMGIC for 2 years were 0.13±0.005 mg, 0.09±0.006 mg, 0.15±0.008 mg and 0.05±0.003 mg, respectively (Groups SDF+RMGIC > SDF+CGIC > CGIC >RMGIC, p < 0.05). The mean ± SD of accumulative silver releasing in SDF+CGIC, CGIC, SDF+RMGIC and RMGIC for 2 years were 0.03±0.009 mg, 0.00±0.00 mg, 0.01±0.003 mg, and 0.00±0.00 mg, respectively (Groups SDF+CGIC > SDF+RMGIC > CGIC&RMGIC, p < 0.05). Groups SDF+CGIC and SDF+RMGIC showed sustainably higher fluoride and silver releasing compared to Groups CGIC and RMGIC (p < 0.05). XRD analysis indicated the fluorapatite and silver chloride were observed only in Groups SDF+CGIC and SDF+RMGIC, but not in Groups CGIC and RMGIC. SEM images of the cross-sectional view of the dentin blocks showed silver crystals within dentinal tubules 1 week and 2-year in Groups with SDF pretreatment. Conclusion: The 38 % SDF dentin pretreatment sustainably increased the fluoride and silver release of GIC and RMGIC restorations for up to 2 years.