Article: Effect of loading rate on shear strength of SnAgCu solder joint

TitleEffect of loading rate on shear strength of SnAgCu solder joint
Authors
Lu, WZhang, NShi, YLei, Y
KeywordsLead-Free Solder
Loading Rate
Shear Strength
Issue Date2010
Citation
Hanjie Xuebao/Transactions Of The China Welding Institution, 2010, v. 31 n. 9, p. 57-60 How to Cite?
AbstractEffect of loading rate on shear strength and fracture mode of SnAgCu (SAC) lead-free solder joint was investigated. The Ag content of the solders used in the experiment was 1% to 3%. The loading rate of the solder joint was 0.01 mm/s to 10 mm/s. The results indicated that the shear strength increased with the increase of loading rate and fracture with ductile feature occured inside the solder, when the loading rate was less than 1 mm/s. When loading rate reached to 10 mm/s, the shear strength decreased and brittle fracture occurred in the intermetallic compounds layer of joint. Moreover, shear strength increased with Ag content of solder increased at low loading rate, while the shear strength of solder joint with 2% Ag was the lowest at high loading rate.
Persistent Identifierhttp://hdl.handle.net/10722/168481
ISSN
0253-360X
2023 SCImago Journal Rankings: 0.186
References
References in Scopus

 

DC FieldValueLanguage
dc.contributor.authorLu, Wen_US
dc.contributor.authorZhang, Nen_US
dc.contributor.authorShi, Yen_US
dc.contributor.authorLei, Yen_US
dc.date.accessioned2012-10-08T03:19:27Z-
dc.date.available2012-10-08T03:19:27Z-
dc.date.issued2010en_US
dc.identifier.citationHanjie Xuebao/Transactions Of The China Welding Institution, 2010, v. 31 n. 9, p. 57-60en_US
dc.identifier.issn0253-360Xen_US
dc.identifier.urihttp://hdl.handle.net/10722/168481-
dc.description.abstractEffect of loading rate on shear strength and fracture mode of SnAgCu (SAC) lead-free solder joint was investigated. The Ag content of the solders used in the experiment was 1% to 3%. The loading rate of the solder joint was 0.01 mm/s to 10 mm/s. The results indicated that the shear strength increased with the increase of loading rate and fracture with ductile feature occured inside the solder, when the loading rate was less than 1 mm/s. When loading rate reached to 10 mm/s, the shear strength decreased and brittle fracture occurred in the intermetallic compounds layer of joint. Moreover, shear strength increased with Ag content of solder increased at low loading rate, while the shear strength of solder joint with 2% Ag was the lowest at high loading rate.en_US
dc.languageengen_US
dc.relation.ispartofHanjie Xuebao/Transactions of the China Welding Institutionen_US
dc.subjectLead-Free Solderen_US
dc.subjectLoading Rateen_US
dc.subjectShear Strengthen_US
dc.titleEffect of loading rate on shear strength of SnAgCu solder jointen_US
dc.typeArticleen_US
dc.identifier.emailLu, W:luwei@hku.hken_US
dc.identifier.authorityLu, W=rp00754en_US
dc.description.naturelink_to_subscribed_fulltexten_US
dc.identifier.scopuseid_2-s2.0-77958110155en_US
dc.relation.referenceshttp://www.scopus.com/mlt/select.url?eid=2-s2.0-77958110155&selection=ref&src=s&origin=recordpageen_US
dc.identifier.volume31en_US
dc.identifier.issue9en_US
dc.identifier.spage57en_US
dc.identifier.epage60en_US
dc.identifier.scopusauthoridLu, W=27868087600en_US
dc.identifier.scopusauthoridZhang, N=7401648579en_US
dc.identifier.scopusauthoridShi, Y=7404964763en_US
dc.identifier.scopusauthoridLei, Y=7201592928en_US
dc.identifier.issnl0253-360X-

Export via OAI-PMH Interface in XML Formats

OR

Export to Other Non-XML Formats