Article: ANNEAL HARDENING IN alpha -BRASS.

TitleANNEAL HARDENING IN alpha -BRASS.
Authors
Issue Date1983
Citation
Metals Technology, 1983, v. 10 pt 3, p. 85-88 How to Cite?
AbstractThe effect of different amounts of prior cold-rolling deformation on the anneal-hardening response of Cu-15Zn, Cu-30Zn, and supersaturated Cu-37Zn has been investigated. Hardness enhancement is small below 40% and easily discernible at rolling strains above 50%. This change is associated with the formation of shear bands. Cold rolling on the order of 5% performed after anneal hardening removes the strength increment and the material then behaves in a manner almost identical to samples not subjected to annealing.
Persistent Identifierhttp://hdl.handle.net/10722/174022
ISSN

 

DC FieldValueLanguage
dc.contributor.authorLee, WBen_US
dc.contributor.authorDuggan, BJen_US
dc.date.accessioned2012-11-14T06:20:18Z-
dc.date.available2012-11-14T06:20:18Z-
dc.date.issued1983en_US
dc.identifier.citationMetals Technology, 1983, v. 10 pt 3, p. 85-88en_US
dc.identifier.issn0307-1693en_US
dc.identifier.urihttp://hdl.handle.net/10722/174022-
dc.description.abstractThe effect of different amounts of prior cold-rolling deformation on the anneal-hardening response of Cu-15Zn, Cu-30Zn, and supersaturated Cu-37Zn has been investigated. Hardness enhancement is small below 40% and easily discernible at rolling strains above 50%. This change is associated with the formation of shear bands. Cold rolling on the order of 5% performed after anneal hardening removes the strength increment and the material then behaves in a manner almost identical to samples not subjected to annealing.en_US
dc.languageengen_US
dc.relation.ispartofMetals Technologyen_US
dc.titleANNEAL HARDENING IN alpha -BRASS.en_US
dc.typeArticleen_US
dc.identifier.emailDuggan, BJ: bjduggan@hkucc.hku.hken_US
dc.identifier.authorityDuggan, BJ=rp01686en_US
dc.description.naturelink_to_subscribed_fulltexten_US
dc.identifier.scopuseid_2-s2.0-0020716431en_US
dc.identifier.volume10en_US
dc.identifier.issuept 3en_US
dc.identifier.spage85en_US
dc.identifier.epage88en_US
dc.identifier.scopusauthoridLee, WB=25952892100en_US
dc.identifier.scopusauthoridDuggan, BJ=7005772998en_US

Export via OAI-PMH Interface in XML Formats


OR


Export to Other Non-XML Formats